Table 2

Result of the analysis of the mechanical properties. is the average of the elastic limits obtained with an offset of 0.2% from the elastic zone; SD (Rp_0:2) is the standard deviation of the elastic limits; is the standard error of the elastic limits; is the average of the Young's moduli; is the standard deviation of Young's moduli; is the standard error of the Young's moduli; and are, respectively, the averages of the elastic limits obtained from the specimens cut at 0° from the rolling direction and at 90°; Similarly, e are the averages of the Young's moduli obtained from specimens cut at 0° from the rolling direction and at 90°.

Temperature (°C)	(MPa)	(MPa)	(MPa)	(GPa)	(GPa)	(GPa)
Room Temp.	107.67	4.34	1.77	65.19	0.46	0.19	1.07	1.02
140	121.10	5.05	2.92	52.83	0.70	0.40	1.02	1.00
180	131.21	1.69	0.98	51.11	1.60	0.92	1.02	1.06
220	161.59	8.93	4.47	48.33	1.18	0.59	0.93	0.97